“A metallurgical degradation mechanism that leads to a reduction in fracture toughness due to long-term exposure in the temperature range of 650°F to 1070°F (345°C to 575°C).”
“It affects Cr-Mo steels and is not easily detected except by impact testing.”
Therefore, option C most accurately defines the condition based on the recognized API description.